  • \( \newcommand{\vecs}[1]{\overset { \scriptstyle \rightharpoonup} {\mathbf{#1}} } \) \( \newcommand{\vecd}[1]{\overset{-\!-\!\rightharpoonup}{\vphantom{a}\smash {#1}}} \)\(\newcommand{\id}{\mathrm{id}}\) \( \newcommand{\Span}{\mathrm{span}}\) \( \newcommand{\kernel}{\mathrm{null}\,}\) \( \newcommand{\range}{\mathrm{range}\,}\) \( \newcommand{\RealPart}{\mathrm{Re}}\) \( \newcommand{\ImaginaryPart}{\mathrm{Im}}\) \( \newcommand{\Argument}{\mathrm{Arg}}\) \( \newcommand{\norm}[1]{\| #1 \|}\) \( \newcommand{\inner}[2]{\langle #1, #2 \rangle}\) \( \newcommand{\Span}{\mathrm{span}}\) \(\newcommand{\id}{\mathrm{id}}\) \( \newcommand{\Span}{\mathrm{span}}\) \( \newcommand{\kernel}{\mathrm{null}\,}\) \( \newcommand{\range}{\mathrm{range}\,}\) \( \newcommand{\RealPart}{\mathrm{Re}}\) \( \newcommand{\ImaginaryPart}{\mathrm{Im}}\) \( \newcommand{\Argument}{\mathrm{Arg}}\) \( \newcommand{\norm}[1]{\| #1 \|}\) \( \newcommand{\inner}[2]{\langle #1, #2 \rangle}\) \( \newcommand{\Span}{\mathrm{span}}\)\(\newcommand{\AA}{\unicode[.8,0]{x212B}}\)

    Example A

    The figure below is a scanning electron micrograph of a niobium carbide dendrite in a Fe-34wt%Cr-5wt%Nb-4.5wt%C alloy. Niobium carbide has a face centred cubic lattice. The specimen has been deep-etched to remove the surrounding matrix chemically and reveal the dendrite. The dendrite has 3 sets of "arms" which are orthogonal to one another (one set pointing out of the plane of the image, the other two sets, to a good approximation, lying in the plane of the image), and each arm has a pyramidal shape at its end. It is known that the crystallographic directions along the dendrite arms correspond to the < 100 > lattice directions, and that the direction ab labelled on the micrograph is [101].

    Scanning electron micrograph of a niobium carbide dendrite in a Fe-34wt%Cr-5wt%Nb-4.5wt%C alloy
    sourced from Dendritic Solidification

    1) If point c (not shown) lies on the axis of this dendrite arm, what is the direction cb ? Index face C , marked on the micrograph.

    alt

    The diagram shows the [101] direction in red. The [100] direction is a < 100 > type direction that forms the observed acute angle with ab, and can be used as cb. Of the < 100 > type directions, we could also have used [001].

    Using a right handed set of axes, we then have z-axis pointing out of the plane of the image, the x-axis pointing along the direction cb, and the y-axis pointing towards the top left of the image.

    Scanning electron micrograph of a niobium carbide dendrite in a Fe-34wt%Cr-5wt%Nb-4.5wt%C alloy

    Face C must contain the direction cb, and its normal must point out of the plane of the image. Therefore face C is a (001) plane.

    2) The four faces which lie at the end of each dendrite arm have normals which all make the same angle with the direction of the arm. Observing that faces A and B marked on the micrograph both contain the direction ab , and noting the general directions along which the normals to these faces point, index faces A and B .

    Both faces A and B have normals pointing in the positive x and z directions, i.e. positive h and l indices. Face A has a positive k index, and face B has a negative k index.

    The morphology of the ends of the arms is that of half an octahedron, suggesting that the faces are (111) type planes. This would make face A, in green, a (111) plane, and face B, in blue, a (111) plane. As required, they both contain the [101] direction, in red.

    Diagram showing dendrite faces

    Example B

    1) Work out the common direction between the (111) and (001) in a triclinic unit cell.

    The relation derived from the Weiss zone law in the section Vectors and planes states that:

    The direction, [UVW], of the intersection of (h1k1l1) and (h2k2l2) is given by:

    \[U = k_{1}l_{2} − k_{2}l_{1}\]

    \[V = l_{1}h_{2} − l_{2}h_{1}\]

    \[W = h_{1}k_{2} − h_{2}k_{1}\]

    We can use this relation as it applies to all crystal systems, including the triclinic system that we are considering.

    We have h1 = 1, k1 = 1, l1 = 1

    and h2 = 0, k2 = 0, l2 = 1

    Therefore

    \[U = (1 × 1) - (0 × 1) = 1\]

    \[V = (1 × 0) - (1 × 1) = −1\]

    \[W = (1 × 0) - (0 × 1) = 0\]

    So the common direction is:

    [110].

    This is shown in the image below:

    Diagram showing common direction

    If we had defined the (001) plane as (h1k1l1) and the (110) plane as (h2k2l2) then the resulting direction would have been, [110] i.e. anti-parallel to [110].

    2) Use the Weiss zone law to show that the direction [110] lies in the (111) plane.

    We have U = 1, V = −1, W = 0,

    and h = 1, k = 1, l = 1.

    \[hU + kV + lW = (1 × 1) + (1 × −1) + (1 × 0) = 0\]

    Therefore the direction [110] lies in the plane (111).


    This page titled 2.9: Worked Examples is shared under a CC BY-NC-SA license and was authored, remixed, and/or curated by Dissemination of IT for the Promotion of Materials Science (DoITPoMS) via source content that was edited to the style and standards of the LibreTexts platform; a detailed edit history is available upon request.